求下面这段命令流的详细解释tb,bkin,1,6 tbtemp,20,1 tbdata,1,278e6,0.1951e11 tbtemp,600,2tbdata,1,141e6,0.155e11 tbtemp,800,3tbdata,1,130e6,0.1314e11 tbtemp,1000,4 tbdata,1,45e6,0.1e11 tbtemp,1200,5 tbdata,1,13e6,0.0595e11tbtemp,1460,6 tbd

求下面这段命令流的详细解释tb,bkin,1,6 tbtemp,20,1 tbdata,1,278e6,0.1951e11 tbtemp,600,2tbdata,1,141e6,0.155e11 tbtemp,800,3tbdata,1,130e6,0.1314e11 tbtemp,1000,4 tbdata,1,45e6,0.1e11 tbtemp,1200,5 tbdata,1,13e6,0.0595e11tbtemp,1460,6 tbd
求下面这段命令流的详细解释
tb,bkin,1,6
tbtemp,20,1
tbdata,1,278e6,0.1951e11
tbtemp,600,2
tbdata,1,141e6,0.155e11
tbtemp,800,3
tbdata,1,130e6,0.1314e11
tbtemp,1000,4
tbdata,1,45e6,0.1e11
tbtemp,1200,5
tbdata,1,13e6,0.0595e11
tbtemp,1460,6
tbdata,1,3E6,0.0002E11

求下面这段命令流的详细解释tb,bkin,1,6 tbtemp,20,1 tbdata,1,278e6,0.1951e11 tbtemp,600,2tbdata,1,141e6,0.155e11 tbtemp,800,3tbdata,1,130e6,0.1314e11 tbtemp,1000,4 tbdata,1,45e6,0.1e11 tbtemp,1200,5 tbdata,1,13e6,0.0595e11tbtemp,1460,6 tbd
首先说明,这段语句是在定义一种材料的双线性随动硬化规律.双线性的含义,就是说材料的应力应变关系是两段直线（双线性）.举下面的第一组数据来说明：tbdata,1,278e6,0.1951e11.这句的含义就是说：屈服应力为1,278e6,切线模量为0.1951e11.光凭这两者还不足以画出材料的应力应变曲线,还需要材料的初始弹性模量ex的值.
 
tb,bkin,1,6                     !bkin指的是bilinear kinematic,1说明是1号材料,6对应下面的6组数据
tbtemp,20,1                                 !第一组数据,温度为20时的应力应变关系
tbdata,1,278e6,0.1951e11          !两个数值分别对应屈服应力和切线模量,以下类似,省略.
tbtemp,600,2                               !第二组数据,温度为600时的应力应变关系
tbdata,1,141e6,0.155e11  
tbtemp,800,3                               !第三组数据,温度为800时的应力应变关系
tbdata,1,130e6,0.1314e11  
tbtemp,1000,4                             !第四组数据,温度为1000时的应力应变关系    
tbdata,1,45e6,0.1e11
tbtemp,1200,5                             !第五组数据,温度为1200时的应力应变关系  
tbdata,1,13e6,0.0595e11
tbtemp,1460,6                             !第六组数据,温度为1400时的应力应变关系 
tbdata,1,3E6,0.0002E11
 
补充说明：
双线性随动硬化的应力应变曲线为：

对上图进行说明：拐点前段的斜率即为ex,弹性模量.拐点的y轴数值即为屈服应力,拐点后半段的斜率即为切线模量.其中T1和T2分别对应不同温度下的不同应力应变曲线.
所以可以断定的是,你上面的语句之前,还必须给出一个弹性模量的数值,否则是不完整的.也就是缺少一句：mp,ex,1,×××.然后才能画出六条不同的曲线.